pro3dure´s GR-18.1 IB : Biocompatible flexible 3D printing resin

287.50

pro3dure´s GR-18.1 IB is a biocompatible 3D printing resin for the generative production of orthodontic ”indirect bonding trays“. The post cured material is flexible, transparent and has a high tear strength.Available in clear transparent color.

Description

pro3dure´s GR-18.1 IB is a biocompatible 3D printing resin for the generative production of orthodontic ”indirect bonding trays“. The post cured material is flexible, transparent and has a high tear strength. This allows the orthodontist to precisely place all brackets in one operation.

COMPATIBLE WITH DLP/LCD/SLA 3D PRINTERS

Technical data

 Colour clear transparent
 Density:  ca. 1.1 g/ml
 Viscosity  ca. 2.4 Pa s
Post cured
material:
(depends
on postcuring unit)
Hardness: ca. 80 Shore A
Storage between 64°F/18°C and 83°F/28°C
Package 1 kg
Typology 405 nm

 

 

.

Specifications

 Property Requirement  Result Standard
 Tensile Strenght   n.a./n.a.*      6.2 MPa DIN  53504
Elongation at break   n.a./n.a.* 50% DIN  53504
Shore Hardness n.a./n.a.* 40D ISO 7619-1
Viscosity (23°C) n.a./n.a.* 2.5 Pa s DIN 53019-1
Biocompatibility Irritation and delayed allergies comply ISO 10993-10
Biocompatibility Citotoxicity comply ISO 10993-5

 

How to use

  • GR-18.1 bottles should be well shaked before use (fig 1).

  • Make sure that GR-18.1 material is temperature adjusted up to 23 °C to 30 °C.

  • Carefully pour GR-18.1 into the vat of the image projection unit (fig 2).

  • Bubbles can be removed with a cleaned spatula or by a recoater routine.

  • If it is possible, always store a bottle GR-18.1 in your production unit in order to avoid temperature differences during refilling.

  • For the build parameter adjustment please refer to the machine data sheet.

  • After the build process is finished a direct post treatment is recommended.

  • If this cannot be guaranteed leave the produced objects in the liquid GR-18.1 resin.

  • After cleaning of the parts with isopropanole ≥ 97 % (approx. 3-5 min. in an ultrasonic bath) the objects are postcured in an adequate light curing unit in a protective gas atmosphere.

  • The dental objects generated out of the generative resin GR-18.1
    can be repaired with GR-18.1 resin.

  • Impurity due to operation mistakes cannot be excluded. With respect to the low viscosity of the resin it is possible to filtrate the GR-18.1 . It is recommended to filtrate and stir up the resin on a regular base (fig 3).

  • To avoid bubbles let GR-18.1 rest for 1 hour before usage.

Important

  • To avoid detrimental effects on material quality do not expose the liquid material to irradiation under any circumstances.

  • Deviations from the described manufacturing process may lead to different mechanical and optical properties of the GR-18.1 material.

  • Ensure personal protective gear during processing.

  • Caution: Polymerised resins are chemically resistant -avoid stains on clothing.

  • Avoid any contact with skin and eyes. In case of accidental contact, rinse with adequate running water, consulting a doctor if necessary.

  • The lot number and the expiration date are indicated on each bottle of GR-18.1 . In case of claims please always indicate the lot number of the product. Do not use the product after expiry of the best before date.

 

.

 

 

Learn more                MSDS

Safety notice

Lumi Industries srl and pro3dure medical GmbH are not liable for any damages caused by improper use and application of the material. To be used on suitable devices by trained specialist personnel for the purpose indicated only.

.

 

Additional information

Weight 1.5 kg
Dimensions 10 × 10 × 30 cm
COLOR

ROSE TRANSPARENT, LIGHT-BLUE TRANSPARENT, CLEAR TRANSPARENT

Reviews

There are no reviews yet.

Be the first to review “pro3dure´s GR-18.1 IB : Biocompatible flexible 3D printing resin”

Your email address will not be published. Required fields are marked *