Liqcreate: Composite-X rigid resin

60.95169.95

Liqcreate Composite-X is an extremely rigid and high performance reinforced nano-micro composite resin for SLA, DLP & LCD / MSLA in the range of 385 – 420nm. Perfect for rapid tooling, wind tunnel testing and industrial applications.

Liqcreate Composite-X is one of the stiffest and strongest material available in the market. It has a flexural modulus over 9000 MPa and a flexural strength of 150 – 170 MPa. The material can be used after UV-post curing, or the properties can be boosted with a thermal cure. This material has features like excellent chemical resistance, high strength and high stiffness.

Clear

Description

Liqcreate Composite-X is an extremely rigid and high performance reinforced nano-micro composite resin for SLA, DLP & LCD / MSLA in the range of 385 – 420nm. Perfect for rapid tooling, wind tunnel testing and industrial applications.

Liqcreate Composite-X is one of the stiffest and strongest material available in the market. It has a flexural modulus over 9000 MPa and a flexural strength of 150 – 170 MPa. The material can be used after UV-post curing, or the properties can be boosted with a thermal cure. This material has features like excellent chemical resistance, high strength and high stiffness.

Technical specifications

Liqcreate Composite-X has a flexural modulus over 9000 MPa and a flexural strength of 150 – 170 MPa. The material can be used after UV-post curing, or the properties can be boosted with a thermal cure. Composite-X features an excellent chemical resistance, high strength and high stiffness, perfect for rapid tooling, wind tunnel testing and industrial applications.

Polymer properties
Mechanical Properties Metric
Description ASTM Method UV curing 60 min. at 60°C UV curing 60 min. at 60°C
thermal curing 120 min. at 100°C
Tensile strength D638 50 – 75 MPa 70 – 85 MPa
Tensile modulus D638 7.5 – 8.5 GPa 8.5 – 9.5 GPa
Elongation at break D638 1% 1%
Flexural strength D790 140 – 150 MPa 150 – 170 MPa
Flexural modulus D790 7.5 – 8.5 GPa 8.5 – 9.5 GPa
IZOD Impact (notched) D256A 19 J/m 18 J/m
Shore D Hardness D2240 93 94
Water sorption D570-98 0.67% 0.59%
Linear Shrinkage during printing Internal method <0.1% <0.1%
Linear Shrinkage during UV-curing Internal Method 0.5% 0.5%
Linear Shrinkage during thermal cure Internal Method 0.1% 0.1%
Compression strength D695 155 MPa 160 MPa
Density solid Internal Method 1.62 g/cm3 1.62 g/cm3
 
Liquid Properties
Description Value
Appearance Opaque white liquid
Viscosity 1400 cps at 25°C
Density 1.52 g/cm3
Ec 9.55 mJ/cm2
Dp metric 0.18 mm
Dp imperial 7.09 mils

More information about Liqcreate Composite-X

Values may vary and depend on individual machine processing and post-curing. For extra details, download the technical data sheet or user guide.

Technical data sheets             Quick guide                  User guide

 

Hazard statements on CLP product label

 
H315: Causes skin irritation.
H317: May cause an allergic skin reaction.
H319: Causes serious eye irritation.
H411: Toxic to aquatic life with long-lasting effects.

Additional information

Weight 1.5 kg
Dimensions 10 × 10 × 30 cm
SIZE

1,5 KG, 0,375 KG

Reviews

There are no reviews yet.

Be the first to review “Liqcreate: Composite-X rigid resin”

Your email address will not be published. Required fields are marked *

Slide to unlock *

This site uses Akismet to reduce spam. Learn how your comment data is processed.