Liqcreate: Elastomer-X elastic resin

46.95129.95

Liqcreate Elastomer-X is a clear photopolymer resin and can be processed on most resin based 3D-printers.

3D-printed parts from this material are exceptionally soft with a Shore A of 43 and has great flexibility. The product can be used as received, or colored with almost any commercial available 3D-resin colorant. Liqcreate Elastomer-X can be used on open DLP, LCD and SLA 3D-printers in the range of 385 – 420nm. Its properties simulate soft TPU and silicone which makes it perfect for the production digital lattice foams, soft end of arm tooling (EOAT) for robots, grommets, bellows and elastic industrial parts.

Clear

Description

Liqcreate Elastomer-X is a clear photopolymer resin and can be processed on most resin based 3D-printers.

3D-printed parts from this material are exceptionally soft with a Shore A of 43 and has great flexibility. The product can be used as received, or colored with almost any commercial available 3D-resin colorant. Liqcreate Elastomer-X can be used on open DLP, LCD and SLA 3D-printers in the range of 385 – 420nm. Its properties simulate soft TPU and silicone which makes it perfect for the production digital lattice foams, soft end of arm tooling (EOAT) for robots, grommets, bellows and elastic industrial parts.

Technical specifications

3D-printed parts from Liqcreate Elastomer-X are exceptionally soft with a Shore A of 43 and mimic soft TPU and silicone properties. Liqcreate Elastomer-X is compatible with open DLP, LCD, MSLA and SLA 3D-printers in the range of 385 – 420nm. Its low hardness of 43 Shore A and elongation up to 180% makes it perfect for the production of digital lattice foams, soft end of arm tooling (EOAT) for robots, grommets, bellows and elastic industrial applications.

Polymer properties
Mechanical Properties UV post-curing
Description ASTM Method Metric[1] Imperial[1]
Tensile strength D638 1.5 MPa 0.22 ksi
Elongation at break D638 140 – 180% 140 – 180%
Tear strength D624 10 – 12 kN/m 10 – 12 kN/m
Compression set 24 hours at 22˚C D395 1% 1%
Shore A Hardness D2240 43 43
Water sorption D570-98 1,5% 1,5%
Glass transition temperature DSC method -5°C 23°F
Degradation temperature Internal method >250°C[2] >482°F[2]
[1]Post-cured 5 minutes with LED curing at 20°C in glycerol or water. These values may vary and depend on individual machine processing and post-curing. 
[2]Discoloration at 140°C, increased rigidity at 220°C – Shore A 54. No cracking in part up to 250°C / 482°F.
 
Liquid Properties 
Description Value
Appearance Clear liquid
Viscosity 2000 cps at 25°C
Density 1.18 g/cm3
Ec  (405nm) 28.48 mJ/cm2
Dp (405nm) 0.28 mm
Ec  (385nm) 26.16 mJ/cm2
Dp (385nm) 0.11 mm

More information about Liqcreate Elastomer-X

Values may vary and depend on individual machine processing and post-curing. For extra details, download the technical data sheet or user guide.

Technical data sheets             Quick guide                  User guide

 

Hazard statements on CLP product label

 
H315: Causes skin irritation.
H317: May cause an allergic skin reaction.
H319: Causes serious eye irritation.
H411: Toxic to aquatic life with long-lasting effects.

Additional information

Weight 1.5 kg
Dimensions 10 × 10 × 30 cm
SIZE

1 KG, 0,25 KG

Reviews

There are no reviews yet.

Be the first to review “Liqcreate: Elastomer-X elastic resin”

Your email address will not be published. Required fields are marked *

Slide to unlock *

This site uses Akismet to reduce spam. Learn how your comment data is processed.