Liqcreate Strong-X is one of the strongest photopolymer resins available in the market. Its flexural strength of 135MPa is comparable to industry’s leading dual-cure cyanate ester resins.
Liqcreate Strong-X is easy to use on open SLA, MSLA and DLP 3D-printers in the range of 385 – 405nm and only requires UV post-curing. This material has excellent features like high strength, high stiffness and high temperature resistance which makes it ideal for injection molding and heavy duty applications.
Technical specifications
Liqcreate Strong-X is one of the strongest photopolymer resins available in the market. Its flexural strength of 135MPa, high stiffness and high temperature resistance which makes it ideal for injection molding and heavy duty applications.
| Mechanical Properties | UV post-curing | ||
|---|---|---|---|
| Description | ASTM Method | High power LED curing
(30 minutes at 60°C) |
High power LED curing
(120 minutes at 60°C) |
| Tensile strength | D638 | 52 – 70 MPa | 60 – 84 MPa |
| Tensile modulus | D638 | 2.9 – 3.2 GPa | 3.1 – 3.4 GPa |
| Elongation at break | D638 | 4 – 8% | 3 – 6% |
| Flexural Strength | D790 | 121 – 130 MPa | 134 – 140 MPa |
| Flexural modulus | D790 | 3.1 – 3.3 GPa | 3.3 – 3.5 GPa |
| IZOD Impact (notched) | D256A | 20 J/m | 17 J/m |
| Shore D Hardness | D2240 | 87 | 90 |
| Water sorption | D570-98 | 0.45% | 0.39% |
| Tg | D7028 | n/a | 128°C |
| Description | Value |
|---|---|
| Appearance | Opaque grey liquid |
| Viscosity | 550 cps at 25°C |
| Density | 1.12 g/cm3 |
| Ec | 9.88 mJ/cm2 |
| Dp metric | 0.20 mm |
| Dp imperial | 7.87 mils |
More information about Liqcreate Strong-X
Values may vary and depend on individual machine processing and post-curing. For extra details, download the technical data sheet or user guide.
Hazard statements on CLP product label
| H315: Causes skin irritation. |
| H317: May cause an allergic skin reaction. |
| H319: Causes serious eye irritation. |
| H411: Toxic to aquatic life with long-lasting effects. |
Reviews
There are no reviews yet.