Description
PRO3dent splint | MSI is ideal for CAM-fabricated hard bite splints. Multi-species inhibition significantly reduces biofilm accumulation and prevents plaque build-up. Available in ocean-blue, in thicknesses of 16 mm and 20 mm (single packaging Ronde 98.5 mm with step).
Advantages:
- high flexural strength
- no discoloration
- highest biocompatibility
- multi-species inhibition (MSI®)
- significant reduction of biofilms
- low plaque accumulation
Specifications for Pro3dure PRO3dent splint | MSI
| Property | Requirement | Result *** | Standard |
| Ultimate flexural strength | ≥ 50 MPa | 68 MPa | ISO 20795-2 ** |
| Flexural modulus | ≥ 1500 MPa | 2600 MPa ** | ISO 20795-2 ** |
| Water solubility | ≤ 5 μg/mm³ | ≤ 5 μg/mm³ | ISO 20795-2 |
| Water sorption | ≤ 5 μg/mm³ | ≤ 35 μg/mm³ | ISO 20795-2 |
| Shore Hardness | n.a./n.a. * | 80 D | ISO 48-4 |
| Bio compatibility | Irritation and delayed-type allergies | Comply |
ISO 10993-1 ISO 10993-10 |
| Bio compatibility | Genotoxicity, Carcinogenity and Reproductive toxicity | Comply |
ISO 10993-1 ISO 10993-3 |
| Bio compatibility | Systemic toxicity | Comply |
ISO 10993-1 ISO 10993-11 |
| Bio compatibility | Cytotoxicity | Comply |
ISO 10993-1 ISO 10993-5 |
* not applicable
** on the basis ISO 20795-2
*** these data result from measurements of a representative sample, which were determined within the scope of our quality assurance
Processing
- PRO3dent splint I MSI milling blanks should be used only for the purpose of CAD/CAM production of dental occlusal splints.
They can be used in all common CAD/CAM systems. - Suitable cross-cut carbide cutters are to be used exclusively for the processing of the PRO3dent splint I MSI material.
- PRO3dent splint I MSI occlusal splints are designed and milled by CAD/CAM technology and qualified staff. After finishing, the thickness in the occlusal region of the splint must not be less than 0,9 mm. For aesthetic reasons, a labial reduction to 0,8 mm is permissible. Any corners and edges should be rounded off.
- PRO3dent splint I MSI splints can be removed from the milling blank by using suitable cross-cut carbide cutters or cutting discs suitable for composites. Carefully cut through the retaining strips
without pressure. - In order to avoid plaque accumulation subsequent polishing of the splints is essential. Please pre-polish with suitable silicone polishers and goat’s hair brushes. The high-luster polishing should be done with a corresponding polishing compound. As far as possible, please avoid heat generation during the polishing and finishing of the PRO3dent splint I MSI splint.
This guarantees the optimal fitting of the splint. - Please note: Upon completion, use an ultrasonic bath with
water at a maximum temperature of approx. 35 °C for cleaning.
Cleaning solutions are not recommended.
Safety notice
The company I.D.M di Marin Davide is not a manufacturer of medical materials or devices. The material sold on this site is neither produced nor controlled by the company I.D.M. di Marin Davide, who in no case can be held responsible for any damage caused by use or application of the material, which must only be used on suitable machines and by specialized personnel, exclusively for the purpose indicated, according to the manufacturer’s instructions. For resins with European certification, the properties of the finished product vary according to the entire printing and post-curing process; refer to the manufacturer for any information about it.