Descrizione
Liqcreate Clear Impact is an optically clear photopolymer resin for SLA, DLP and MSLA technologies in the range of 385 – 405nm. Parts created with Liqcreate Clear Impact are perfectly transparent after post-processing, slightly flexible and have an excellent impact resistance.
The high toughness of this clear resin makes it ideal for the production of clear and transparent functional parts which are repeatedly exposed to stress. Low water absorption, weather resistance and low yellowing properties, makes it perfect for outdoor and display applications.
Technical specifications
Liqcreate Clear Impact is a clear engineering resin and perfectly transparent after post-processing. The good toughness of this clear resin makes it ideal for the production of functional parts which are repeatedly exposed to stress. Low water absorption and weather resistance makes it perfect for outdoor applications.
| Mechanical Properties | UV post-curing | ||
|---|---|---|---|
| Description | ASTM Method | Metric | Imperial |
| Tensile strength | D638 | 47 MPa | 6.8 ksi |
| Tensile modulus | D638 | 1.4 GPa | 203 ksi |
| Elongation at break | D638 | 15-25% | 15-25% |
| Flexural strength | D790 | 58 MPa | 8.4 ksi |
| Flexural modulus | D790 | 1.7 GPa | 247 ksi |
| IZOD Impact (notched) | D256A | 31 J/m | 0.58 ft-lb/in |
| Shore D Hardness | D2240 | 68 | 68 |
| Water sorption | D570-98 | 0.50% | 0.50% |
| Description | Value |
|---|---|
| Appearance | Colorless clear liquid |
| Viscosity | 1000 cps at 25°C |
| Density | 1.12 g/cm3 |
| Ec | 13.96 mJ/cm2 |
| Dp metric | 0.17 mm |
| Dp imperial | 6.69 mils |
More information about Liqcreate Clear Impact
Values may vary and depend on individual machine processing and post-curing. For extra details, download the technical data sheet or user guide.
Hazard statements on CLP product label
| H315: Causes skin irritation. |
| H317: May cause an allergic skin reaction. |
| H319: Causes serious eye irritation. |
| H413: May cause long-lasting harmful effects to aquatic life. |
Recensioni
Ancora non ci sono recensioni.